Title: Solution blown nanofibrous membrane for microfiltration

Authors: Xupin Zhuang a,b , Lei Shi a , Kaifei Jia a , Bowen Cheng b,n , Weimin Kang

Abstract: Nanofibrous membranes have been paid attention in microfiltration. Solution blowing process is a new nanofiber fabricating method with high productivity. In this study, polyvinylidene fiuoride (PVDF) nanofibrous mat was successfully solution blown using a multiorifices die. The fibers were mostly 60 280 nm in diameter and three-dimensional curly which resulted in a loose construction with high porosity of 95.8%. The nanofibrous mat was further hot-pressed to increase its integrality. The structure and microfiltration performance was evaluated. The results showed the crystallinity of the membranes increased, the porosity and pore size decreased after hot-pressing treatment. The hot-pressed membranes showed high retention ratio against microparticles and high pure water fiux which will help the solution blown membrane find application in high fiux microfiltration.   

Publish Year: 2013

Published in: Journal of Membrane Science - Science Direct

Number of Pages: 5

موضوع: فناوری نانو

مشاهده صفحه اول مقاله

دانلود مقاله

مشاهده مقاله در سایت ناشر

 

ایران سای – مرجع مقالات علمی فنی مهندسی

حامی دانش بومی ایرانیان

 



برچسب ها : دانلود مقاله ، دانلود رایگان مقاله IEEE ، یوزرنیم و پسورد سایتهای علمی ، یوزرنیم و پسورد دانشگاه های معتبر ، دانلود مقاله آی اس آی ، دانلود رایگان مقاله مهندسی ،
ارسال نظر
نام شما :
آدرس وب سایت :
پست الکترونیک :
پیام شما :
کد امنیتی :




آمار وبلاگ
  • افراد آنلاین : 1
  • بازدید امروز : 2
  • بازدید دیروز : 6
  • بازدید این هفته : 21
  • بازدید این ماه : 106
  • بازدید امسال : 8651
  • بازدید کل : 75068
  • تعداد پست ها : 127
  • تعداد نظرات : 0